This site uses and sets "cookies" on your computer to help make this website better. You can learn more about these cookies and general information about how to change your cookie settings by clicking here.By continuing to use this site without changing your settings, you are agreeing to our use of cookies.

Home / Products / Seamless Flooring / EPOXY FLOOR COAT

  • 5
  • 25
  • 3201
  • 5
  • 25
  • 3201

Solvent-free Epoxy Intermediate Coat - EPR3201 (A/B)Two-component coating composed of premium Nanya epoxy resin, high-efficiency surface additives, high-quality pigments, and curing agents and other raw materials.

Model Number: EPR3201 (A/B)

Component: premium Nanya epoxy resin, high-efficiency surface additives, high-quality pigments, and curing agents and other raw materials.

Certificate: France A+, CE, Rohs, ISO9001

Design use: an intermediate coat material for leveling the base surface or preparing a pressure-resistant load-bearing layer and effectively improving the hardness and flatness of the base surface, keeping color matching with topcoat, improving hiding power of topcoat layer, and reducing the amount of topcoat.

Appearance: Main agent: Color adjustable

Curing agent: Light brown transparent

Blend ratio: A:B = 5:1 mass ratio

Storage time: 1 year

Storage temperature: 5℃-35℃

Packaging specification:Paint:25KG      Curing agent:5KG

Main Features

Solvent-free, non-toxic and eco-friendly

Low viscosity, large sand ratio, good leveling

Excellent strength resistance and color retention


3101,3201,3301


Application Scenarios

Perflex Solvent-free Epoxy Intermediate Coat EPR3201 is primarily intended as a versatile material, mainly designed to mix quartz sand with a proportion of no more than 30% to make epoxy mortar. It can be also added with quartz powder with a proportion of no more than 20% to prepare epoxy putty, which can be used for leveling the base surface or preparing a pressure-resistant load-bearing layer. EPR3201 can effectively improve the hardness and flatness of the base surface, keep the color matching with topcoat, improve the hiding power of the topcoat layer, and reduce the amount of topcoat.


3201-FLAKE版



Physical Parameters

Main Agent

Curing Agent

Appearance: Colorless adjustable

 Appearance: light brown transparent

Viscosity 25℃:1300MPaS

Viscosity 25℃:150MPaS

Specific gravity 25°C: 1.45

Specific gravity 25°C:1.0

Solids:100%  

Solids:100%  


Technical Indicators

Pot life/min

40 (10)

25 (25)

20 (35)

Gel time/h

8 (10)

5 (25)

4 (35)

Tack free/h

16 (10)

10 (25)

8 (35)

Recoat/h

12 (10)

8 (25)

6 (35)


Physical Properties After Curing

Paint appearance

Normal

Adhesion to epoxy primer

3MPa

Shore D Hardness (7 days at room temperature)

75

Compressive strength

80MPa

Impact resistant (500g, 1m)

Pass

Density g/cm3

1.35-1.45 (part A)

Density g/cm3

1.05 (part B)


Construction Parameters

Blend ratio     A: B = 5:1   mass ratio

Construction dosage: Above 0.5kg/m2

Construction conditions

Ambient temperature: 10℃-35℃,   Ambient humidity: ≤75%

Substrate temperature: must be greater than the air dew point temperature 3℃ or more.

Cleaning agent: epoxy thinner

The above data is for guidance only. The actual drying time/interval time before coating can be longer or shorter depending on the film thickness of the coating, ventilation condition, temperature and humidity, etc.

Color Selection

HIDE THE FULL COLOR SELECTION

岩片图

Perflex pick Tools

Perflex pick Tools
Use it with our product…
And make your project easier

Favorable Effect By Product

Product Information Download

Technical Data SheetDownload

More Relative Products

Leave your inquiry

Name

Email Address

Contact number

Description

tel+86 183 9099 2093

email[email protected]

whatsapp

#

contact

Solvent-free Epoxy Intermediate Coat - EPR3201 (A/B)

Solvent-free Epoxy Intermediate Coat - EPR3201 (A/B)

Model Number:EPR3201 (A/B)

Component:premium Nanya epoxy resin, high-efficiency surface additives, high-quality pigments, and curing agents and other raw materials.

Design use:an intermediate coat material for leveling the base surface or preparing a pressure-resistant load-bearing layer and effectively improving the hardness and flatness of the base surface, keeping color matching with topcoat, improving hiding power of topcoat layer, and reducing the amount of topcoat.

Leave a Message
We will call you back soon!